Analisis Baja S55C Terhadap Suhu Pemanasan Dan Media Pendingin Pada Proses Hardening
DOI:
https://doi.org/10.33504/jitt.v3i2.332Keywords:
Heat Treatment, Hardening, S55C SteelAbstract
The carbon steel chosen for this research is S55C steel which is medium or medium carbon steel. The hardening process is a heat treatment process carried out with the aim of increasing the natural hardness of metal or steel. This process is carried out at high temperatures, namely at the austenization temperature which is used to dissolve cementite in austenite which is then quenched quickly. The method used in this research is experimental. The parameters used in this research were temperatures of 880°C, 950°C, and 1020°C and used seawater, salt water, and oil as cooling media. Based on the hardness test results after the hardening process, the combination of temperature 1020°C and sea water produces the lowest average hardness, namely 24.8 HRC, and the combination of temperature 1020°C and salt water produces the highest average hardness, namely 40.
Downloads
References
. Wikipedia, “Klasifikasi Baja,” 22 Maret 2023 [Online]. Available https://bundaliainsidi.blogspot.com/2015/11/baja-karbon.html
. Mukaddis, A. (2023). Analisis Pengaruh Variasi Temperatur Hardening Terhadap Kekerasan, Keausan Pahat HSS Dan Kekasaran Permukaan Benda Kerja Pada Proses Pembubutan ST41-Submit Jurnal (Doctoral dissertation, Institut Teknologi Kalimantan).
. Nugroho, E., Handono, S. D., Asroni, A., & Wahidin, W. (2019). Pengaruh Temperatur dan Media Pendingin pada Proses Heat Treatment Baja AISI 1045 terhadap Kekerasan dan Laju Korosi. Turbo: Jurnal Program Studi Teknik Mesin, 8(1).
. Jaelani, M. A., Sidiq, M. F., & Wilis, G. R. (2021). Analisa Penguatan Mata Pisau Mesin Pencacah Sampah Organik Dengan Proses Heat Treatment Bertingkat. Jurnal Crankshaft, 4(1), 93-102.
. Munandar, M. H. A., Kardiman, K., & Santoso, D. T. (2023). Pengaruh Variasi Holding Time Pada Proses Heat Treatment (Hardening) Untuk Baja S50c Sebagai Pisau Mesin Pencacah Kayu. Jurnal Mesin Nusantara, 6(2), 127-136.
. Ghaddafi, M. (2021). Pengaruh Media Air Garam Terhadap Kekerasan Dari Proses Perlakuan Panas Menggunakan Api Oksi Asetilen (Doctoral dissertation, Universitas Islam Riau).
. Zayadi, A., & Setyawan, E. (2022). Pengaruh Waktu Tempering terhadap Karakter Baja s45c Pasca Quenching pada 950oc dan Tempering 500 C. Jurnal Teknologi Kedirgantaraan, 7(1).
. ISWORO, H. (2020). Pengaruh Variasi Temperatur Pemanasan Dan Media Pendingin Terhadap Kekerasan dan Struktur Mikro Baja ST 41 Metode Hardening.
. Bagus Ilham, P. (2022). PENGARUH TEMPERATUR DAN MEDIA PENDINGIN PADA PROSES HEAT TREATMENT TERHADAP SIFAT MEKANIS BAJA S45C UNTUK APLIKASI MATA POTONG PENCACAH PLASTIK (Doctoral dissertation, Politeknik Manufaktur Negeri Bangka Belitung).
. Nasional-BATAN, B. T. A. Pengaruh Waktu Tempering terhadap Karakter Baja s45c Pasca Quenching pada 950oc dan Tempering 500oc.
. Agung, A. A. R., Kurniawan, E. D., & Hermawan, R. (2023). Pengaruh Variasi Media Pendingin Quenching Terhadap Kekerasan Baja Aisi 1045. Jurnal Pendidikan Teknik Mesin Undiksha, 11(1), 124-130.
.Yudo, E. (2022). ANALISIS KEKERASAN BAJA S45C DENGAN PROSES HEAT TREATMENT UNTUK PENGGUNAAN BAHAN PISAU CRUSHER PENCACAH PLASTIK. Manutech: Jurnal Teknologi Manufaktur, 14(02), 86-93.
.Hasanuddin, H., Hartono, P., & Lesmanah, U. (2023). Analisis Pengaruh Variasi Temperatur Heat Treatment dan waktu Perendaman Baja SS 400 Terhadap Laju Korosi. Jurnal Teknik Mesin, 20(4), 258-263.
. Halim, A., Subhan, M., & Kurniawan, Z. (2022, February). STUDI EKSPERIMEN PENGARUH SUHU HARDENING
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2025 Jurnal Inovasi Teknologi Terapan
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.