Analisa Kekuatan Impak Sambungan Las Gesek Dengan Variasi Waktu Pada Dua Material Baja Aisi 1040 Dengan SS 400
DOI:
https://doi.org/10.33504/jitt.v1i1.71Keywords:
Aisi 1040 steel, Impact, Friction welding, RSM, ss 400 steeAbstract
Welding plays an important role in every metal working and repair in the production process. There are various methods to overcome problems in the meterial connection process. One of them is friction welding which is one of the solutions in solving metal joining problems. In this study, the method used is the RSM (Response Surface Method) method which aims to determine the value of impact strength on AISI 1040 steel which is connected to SS 400 steel which has been carried out the Friction Welding process. This study uses an impact test in accordance with the standard ASTM E23 impact test charpy method with a size of 55 mm × 10 mm × 10 mm with a notch depth of 2 mm, and a notch angle of 45 °. The impact test was conducted using the Charpy method impact testing machine model JB-300B. With a pendulum capacity of 150 Joules. Based on the results of the impact test, the largest value was obtained in the 6th and 7th experiments with an impact price value of 2.575 joules/mm2, while the smallest value was in the 3rd experiment with a value of 1.557 joules/mm2
Downloads
References
Bilal, N. I. (2021). Pengaruh Variasi Arus Busur Listrik Pengelasan Gmaw Terhadap Kekuatan Impak Pada Baja Karbon Rendah ST 37 (Doctoral dissertation, Politeknik Manufaktur Negeri Bangka Belitung).
VIHARDI, H., & Arifin, A. (2019). Analisis Sifat Mekanik Dan Mikrostruktur Pada Pengelasan Stainless Steel Dengan Baja Karbon Rendah Menggunakan Metode Friction Welding (Doctoral dissertation, Sriwijaya University).
Sai'in, A. (2016). Pengaruh Kecepatan Putar, Gaya Gesek, Waktu Gesek Terhadap Kekerasan, Kekuatan Impak, Laju Korosi Dan Struktur Mikro Hasil Lasan Proses Las Gesek Material Berbeda Baja SUH 3 DAN SUH 35 (Doctoral dissertation, Institut Teknologi Sepuluh Nopember).
Selvakumar, N. (2017). Microstructure, Surface Topography And Sliding Wear Behaviour Of Titanium Based Coating On AISI 1040 Steel By Magnetron Sputtering. Archives Of Civil And Mechanical Engineering, 17(2), 281-292.
Rizal, Y. (2017). Peningkatan Kekuatan Tarik Baja Karbon Aisi 1040 Akibat Pengaruh Media Pendingin Pada Proses Perlakuan Panas. Jurnal APTEK, 9(1), 71-78.
Abidah, A. F., & Drastiawati, N. S. (2019). Analisis SS400 Hasil Carburizing Media Arang Tempurung Kelapa-Baco3 Dengan Variasi Temperatur Pemanasan Dan Holding Time Ditinjau Dari Pengujian Kekerasan Dan Struktur Mikro. Jurnal Teknik Mesin, 7(2).
Al Ghifari, I., Budiarto, U., & Zakki, A. F. (2018). Analisa Kekuatan Impak, Tarik, dan Mikrografi Aluminium 5083 Akibat Pengelasan MIG (Metal Inert Gas) dengan Variasi Posisi Pengelasan. Jurnal Teknik Perkapalan, 6(4).
Montgomery, D.C. 2001. Design and Analysis of Experiments. USA: John Wiley & Sons, Inc.
Ratnawati, S. E., Ekantari, N., Pradipta, T. W., & Pramita, B. L. (2018). Aplikasi Response Surface Methodology (RSM) Pada Optimasi Ekstraksi Kalsium Tulang Lele (The Application Of Response Surface Methodology (RSM) On The Optimization Of Catfish Bone Calisum Extaction. Jurnal Perikanan Universitas Gajah Mada, 20, 41-8.
Meilianto, A., Rodika, R., & Rivai, M. (2022, February). Pengaruh Variasi Waktu Gesek Pada Pengelasan Gesek (Friction Welding) Terhadap Kekuatan Impak Baja ST37. In Seminar Nasional Inovasi Teknologi Terapan (Vol. 2, No. 01, Pp. 374-380).
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2023 Jurnal Inovasi Teknologi Terapan
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.