Pengaruh Foaming Agent Terhadap Porositas dan Densitas Cellular Lightweight Concrete
DOI:
https://doi.org/10.33504/jitt.v1i1.79Keywords:
Cellular Lightweight Concrete , Foaming agent, Density, PorosityAbstract
With the rapid development of the industry at this time emerged a variety of technologies that developed, one of which was the food and beverage industry. The use of plastic in packaging is one of the reasons for the accumulation of waste. Handling that can be done is to process the plastic waste into one of the materials added to manufacture lightweight bricks. Lightweight brick is a material that has a lower mass than conventional brick. This study aimed to determine the effect of foaming agent variations on the density and porosity of lightweight bricks and to prove the hypothesis that variations in foaming agent affect density and porosity by analysis of variance. The test objects in this study were in the form of blocks of 100 mm × 50 mm × 50 mm in 27 variations and with three replications with 81 samples of the test objects. From this research, the best density value was 666.72 kg/m3 using an 85 cm3 foaming agent with porosity values ranging from 0.01 to 0.42%.
Downloads
References
T. Istirokhatun and W. D. Nugraha, "PELATIHAN PEMBUATAN ECOBRICKS SEBAGAI PENGELOLAAN SAMPAH PLASTIK DI RT 01 RW 05, KELURAHAN KRAMAS, KECAMATAN TEMBALANG, SEMARANG," JURNAL PASOPATI, vol. 1, no. 1, p. 85, 2019.
S. S. Raees, g. M. Shahid, S. Ayyan, S. M. Anas, P. A. Hafiz and A. AbdulHaq, "Cellular Light Weight Concrete," International Research Journal of Engineering and Technology (IRJET), vol. 6, no. 4, p. 3212, April 2019.
R. Suryanita, Y. Firzal, H. Maizir, I. Mustafa and M. F. B. Arshad, "EXPERIMENTAL STUDY ON PERFORMANCE OF CELLULAR LIGHTWEIGHT CONCRETE DUE TO EXPOSURE HIGH TEMPERATURE," International Journal of GOMATE, vol. 21, no. 83, p. 20, July 2021.
D. Arita, A. Kurniawandy and H. Taufik, "TINJAUAN KUAT TEKAN VATA RINGAN MENGGUNAKAN BAHAN TAMBAH FOAMING AGENT," Jom FTEKNIK, vol. 4, no. 1, p. 4, Februari 2017.
R. Suryanita, Perilaku Mekanik Bata Ringan Cellular Lightweight Concrete dengan Penambahan Silica Fume, PEKANBARU: UR Press, 2020.
N. Sumbawaty, S. Ahzan and D. S. B. Prasetya, "Uji Porositas dan Kuat tekan Batako Ringan Berbahan Dasar Limbah Pengolahan Emas (LPE) dengan Filler Pohon Pisang (FPP)," Jurnal Penelitian dan Pengkajian Ilmu Pendidikan : e-Saintika, vol. 1, no. 2, p. 89, June 2018.
M. Hisyam and F. Widyawati, "ANALISIS PENGARUH MASSA SERAT TERHADAP SIFAT FISIS DAN MEKANIK PAPAN KOMPOSIT GIPSUM BERPENGUAT SISAL (AGAVE SISALANA)," HEXAGON, vol. 2, no. 1, p. 18, Januari 2021.
D. Arita, A. Kurniawandy and H. Taufik, "TINJAUAN KUAT TEKAN BATA RINGAN MENGGUNAKAN BAHAN TAMBAH FOAMING AGENT," Jom FTEKNIK, vol. 4, no. 1, p. 3, Februari 2017.
I. Okatama, "ANALISA PELEBURAN LIMBAH PLASTIK JENIS POLYETHYELENE TERPHTALATE (PET) MENJADI BIJI PLASTIK MELALUI PENGUJIAN ALAT PELEBUR PLASTIK," Jurnal Teknik Mesin (JTM), vol. 5, no. 3, p. 22, Oktober 2016.
T. K. M. B. and J. T. , "PENENTUAN MORFOLOGI PERMUKAAN DAN SIFAT FISIS SERTA SIFAT MEKANIK BATU BATA ASAL TANAH MERAH KABUPATEN KUPANG NUSA TENGGARA TIMUR," Jurnal Fisika Sains dan Aplikasinya, vol. 2, no. 2, p. 94, Oktober 2017.
M. I. Alim, A. Firdausi and M. D. Nurmalasari, "Densitas dan Porositas Batuan," LAPORAN PRAKTIKUM FISIKA MATERIAL, p. 1, 2017.
I.A. Wahyudie, R. Soenoko, W. Suprapto and Y.S. Irawan, "Enhancing hardness and wear resistance of ZrSiO4-SnO2/Cu10Sn composite produced by warm compaction and sintering", Metalurgija, vol.59, no. 1, pp. 27-30, 2020. [Online]. Available: https://hrcak.srce.hr/224746. [Accessed: 18 January 2023]
Ilham Ary Wahyudie et al 2019 IOP Conference Series: Materials Science and Engineering. 494. 012101 Doi: 10.1088/1757-899X/494/1/012101
Douglas C. Montgomery, Design of Analysis of Experiments. Arizona, 2009.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2023 Jurnal Inovasi Teknologi Terapan
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.